Non-leafing Metallic Sparkle Aluminum Paste | Aluminum Pigment
|
Grade |
Non- Volatile Content (±2%) |
D50 Value (±2μm) |
Screen Analysis |
Specific Gravity approx. (g/cm3) |
Solvent |
||
|
|
|
|
<100μm min. % |
<60μm min. % |
<45μm min. % |
|
|
|
LS355 |
70 |
55 |
99.0 |
-- |
-- |
1.4 |
MS/SN |
|
LS352 |
70 |
52 |
99.0 |
-- |
-- |
1.4 |
MS/SN |
|
LS350 |
70 |
50 |
99.0 |
-- |
-- |
1.4 |
MS/SN |
|
LS345 |
70 |
45 |
-- |
99.0 |
-- |
1.4 |
MS/SN |
|
LS342 |
70 |
42 |
-- |
99.0 |
-- |
1.4 |
MS/SN |
|
LS336 |
70 |
36 |
-- |
99.0 |
-- |
1.4 |
MS/SN |
|
LS332 |
70 |
32 |
-- |
99.0 |
-- |
1.5 |
MS/SN |
|
LS328 |
70 |
28 |
-- |
-- |
99.0 |
1.5 |
MS/SN |
|
LS324 |
70 |
24 |
-- |
-- |
99.0 |
1.5 |
MS/SN |
|
LS316 |
70 |
16 |
-- |
-- |
99.9 |
1.5 |
MS/SN |
|
LG285 |
70 |
85 |
98.5 |
-- |
-- |
1.5 |
MS/SN |
|
LG268 |
70 |
68 |
98.5 |
-- |
-- |
1.5 |
MS/SN |
|
LG260 |
70 |
60 |
98.5 |
-- |
-- |
1.5 |
MS/SN |
|
LG257 |
70 |
57 |
99.0 |
-- |
-- |
1.5 |
MS/SN |
|
LG240 |
70 |
40 |
-- |
98.5 |
-- |
1.5 |
MS/SN |
|
LG235 |
70 |
35 |
-- |
99.0 |
-- |
1.5 |
MS/SN |
|
LG232 |
70 |
32 |
-- |
99.0 |
-- |
1.5 |
MS/SN |
|
LG230 |
70 |
30 |
-- |
-- |
-- |
1.5 |
MS/SN |
|
LG223 |
70 |
23 |
-- |
-- |
99.5 |
1.5 |
MS/SN |
|
LG220 |
70 |
20 |
-- |
-- |
99.5 |
1.5 |
MS/SN |
Aluminum Paste can be divided into two categories: leafing type and non-leafing type. During the grinding process, one fatty acid is replaced by another, which makes the Aluminum Paste have completely different characteristics and appearance, and the shapes of Aluminum flakes are snowflake, fish scale and silver dollar. Mainly used in automotive coatings, weak plastic coatings, metal industrial coatings, marine coatings, heat-resistant coatings, roofing coatings and so on. It is also used in plastic paint, hardware and home appliance paint, motorbike paint, bicycle paint and so on.
The series are made of high pure raw material, performing excellent metallic and sparkle effect.
-
-
-
They are mainly used in plastics coatings, automotive, motorcycle, helmet and high quality industrial coatings.
-
-
- 1.Please make sure to confirm the sample before each use of Aluminumsilver paste.
- 2.When dispersing Aluminum-silver paste, use the pre-dispersing method: choose the appropriate solvent first, add the solvent into the Aluminum-silver paste with the ratio of Aluminum-silver paste to solvent as 1:1-2, stir it slowly and evenly, and then pour it into the prepared base material.
- 3.Avoid using high-speed dispersing equipment for a long time during the mixing process.
- 1.The silver Aluminumpaste should keep the container sealed and the storage temperature should be kept at 15°C-35°C.
- 2.Avoid direct exposure to direct sunlight, rain and excessive temperature.
- 3.After unsealing, if there is any remaining silver Aluminumpaste should be sealed immediately to avoid solvent evaporation and oxidation failure.
- 4.Long-term storage of Aluminumsilver paste may be solvent volatility or other pollution, please re-test before use to avoid loss.
- 1.In case of fire, please use chemical powder or special dry sand to extinguish the fire, do not use water to extinguish the fire.
- 2.If Aluminumsilver paste accidentally gets into eyes, please flush with water for at least 15 minutes and seek medical advice.